Sgcu-Cusi3 D100 D200 D300 Copper Alloy Welding Wire

Model NO.
ERCUSI-A
Slag Characteristic
Acidic
Extended Length
>20mm
Transport Package
1kg/5kg/10kg/15kg
Specification
0.8/0.9/1.0/1.2/1.6/2.0/2.5/5.0
Trademark
HENGTAI
Origin
Tongling
Production Capacity
200mts
Reference Price
$ 9.70 - 98.10
Contact Us

Product Description


 

Product Description

Copper alloy welding wire Silicon Bronze TIG Welding rod AWS A5.8 ERCuSi-A CuSi3 GTAW for argon arc welding
 

CHEMICAL COMPOSITION(%)
Standard Class Alloy Cu Al Fe Mn Ni P Pb Si Sn Zn Other
ISO24373 Cu6560 CuSi3Mn1 bal. 0.02 0.5

0.5~

1.5

- 0.05 0.02

2.8~

4.0

0.2 0.4 0.5
GB/T9460 SCu6560 CuSi3Mn bal.

max

0.01

max

0.5

max

1.5

- -

max

0.02

2.8~

4.0

max

1.0

max

1.0

max

0.5

BS EN14640 Cu6560 CuSi3Mn1 bal. 0.01 0.5

0.5~

1.5

- 0.02 0.02

2.8~

4.0

0.2 0.2 0.4
AWS A5.7 C65600 ERCuSi-A bal. 0.01 0.05 1.5 - - 0.02

2.8~

4.0

1.0 1.0 0.50
DIN 1733 2.1461 SG-CuSi3 bal.

max

0.01

max

0.3

0.5~

1.5

-

max

0.02

max

0.02

2.8~

4.0

max

0.2

max

0.2  

max

0.4

Sgcu-Cusi3 D100 D200 D300 Copper Alloy Welding Wire
TRADE MARK S211
Equivalent to AWS ERCuSi-A
Characteristics Good mechanical properties
Good corrosion resistance
Welding Method GTAW
Argon arc welding
Application Used for TIG,Excellent for plain or coated steels.Also used for sufacing arears subjected to corrossion.

Introduction:

Best for butt and the hard facing of brass,especially for the MIG welding of zinc coated steel sheet.Pre-heat suggested when MIG hard facing for large size products and use pulsed argon arc welding while hard facing on steel.
Sgcu-Cusi3 D100 D200 D300 Copper Alloy Welding Wire

 

Sgcu-Cusi3 D100 D200 D300 Copper Alloy Welding Wire
Physical Properties and Mechanical Properties:
Solids-Temperature 910ºC
Liquids-Temperature 1025ºC
Density 8.5kg/dm 3
Tensile Strength 330-370N/mm 2
Elongation 40%
Brinell Hardness 80-95HB
Phosphor Bronze CUSN8P
CHEMICAL COMPOSITION(%) 
Standard Class  Alloy Cu  Al  Fe  Mn Ni P  Pb  Si  Sn  Zn  Other 
ISO24373  Cu5210  CuSn8P bal. - 0.1  - 0.2

0.01~

0.4 

0.02 - 

7.5~

8.5

0. 2 0.2
GB/T9460  SCu5210  CuSn8P  bal.

- 

max

0.1

- 

max

0.2

 0.01~

0.4 

max

0.02 

- 

7.5~

8.5

max

0. 2

max

0.2

BS EN14640  Cu5210  CuSn9P  bal.  -  0.1  -  - 

0.01~

0.4 

 0.02 - 

7.5~

9.0

0.2  0.5
AWS A5.7  C52100  ERCuSn-C bal.  0.01  0.10 -  - 

 0.10~

0.35

0.02  -

7.5~

9.0

0. 2

0.50
Physical Properties and Mechanical Properties:
Solid-Temperature 875ºC  Liquids-Temperature     1025ºC  
Density  8.8kg/dm 3  Tensile Strength 260N/mm 2    
Elongation  20%  Brinell Hardness  80HB 
Introduction:

Recommended for the welding of copper with Cu-Sn alloy.Best for the butt joining welding of brass with steel.Pre-heat suggested for the large size Products,and pulsed argon arc welding is recommended for multilayer hard facing on steel.

Sgcu-Cusi3 D100 D200 D300 Copper Alloy Welding Wire
Sgcu-Cusi3 D100 D200 D300 Copper Alloy Welding Wire

PRODUCTS APPLICATION


Our products are suitable for automobile casting, high pressure valve iron, hydraulic rod, marine casting, aerospace casting,ocean exploration, precision machinery, deep sea scale, marine water scale, high pressure valve, etc. Our company is a world leader in the field of copper alloys, and has made outstanding contributions to the field of copper alloy welding in the world.Our company has been to Arabia, Dubai, Germany, the United States, France, the Middle East, and Vietnam for many times to conduct academic exchanges and promote the world. Development in the field of copper alloy welding.
Sgcu-Cusi3 D100 D200 D300 Copper Alloy Welding Wire

CONTACT US

 






 

 

Welding Wire

GOUV.NE, 2023