Outstanding Weathering Resistance Ployester Resin for Metals Coating I-902

Model NO.
I-902
Color
White
Viscosity
4000-5000cps
Acid Value
30-35mgkoh/G
Product Appearance
White Particles
Curing Conditions
200ºC/10min
Characteristic
Good Adhesion,Good Weather Resistance
Tg
Greater Than or Equal to 64
Application
Powder Coating
Type
Powder Coating Resins
Transport Package
PE Bag
Specification
25KG/Bag
Trademark
AquaCity
Origin
China
HS Code
3907999990
Production Capacity
15000tons/Year
Package size per unit product
53.00cm * 39.00cm * 14.00cm
Gross weight per unit product
25.000kg
Reference Price
$ 1.63 - 1.81
Contact Us

Product Description

Outstanding Weathering Resistance Ployester Resin for Metals Coating I-902 Outstanding Weathering Resistance Ployester Resin for Metals Coating I-902 Outstanding Weathering Resistance Ployester Resin for Metals Coating I-902 Outstanding Weathering Resistance Ployester Resin for Metals Coating I-902 Outstanding Weathering Resistance Ployester Resin for Metals Coating I-902
 
Curing Agent Triglycidyl Isocyanurate(TGIC)
Hydroxy alkyl amide(HAA)
Type of Resins  Item No. Ratio
PE/Crosslinker 		Acid Value
(mgKOH/g) 		Viscosity(p/200ºC)
/mpa.s 		Tg Value
(°C) 		Cure cycle
ºC/min 		Key Features
TGIC Based Polyester Resins I902 93/7 30~35 4000~5000 ≥64 200*10 High gloss ,Excellent flow, weathering resistance and mechanical properties
I903 93/7 30~35 4500~5500 ≥62 200*10 Super weathering resistance, Excellent mechanical properties,good flow
I906 93/7 30~35 4000~5000 ≥65 200*10 High gloss ,Excellent flow, boiling water resistance, mechanical properties
I907 93/7 29~35 5000~6000 ≥67 200*10 Good weathering resistance and mechanical properties,,suitable for texture powder coating 
I801 96/4 18~24 5500~6500 ≥65 200*10 For dry blend matte system as fast component,good storage stability
I802 93/7 30~36 3800~4800 ≥65 200*10 Excellent flow,suitable for High gloss and matt
I808 90/10 48~55 2800~3800 ≥66 200*10 For dry blend matte system as fast component,good storage stability
I301 96/4 18~24 5000~6000 ≥65 200*10
Low cost resin,for dry blend matte system as fast component,good storage stability
I303 93/7 30~36 3600~4600 ≥64 200*10 Low cost resin,good flow and mechanical properties
I307 93/7 30~35 4800~6000 ≥65 200*10 Low cost resin,suitable for texture powder coating
I308 90/10 50~55 2600~3600 ≥65 200*10
Low cost resin,for dry blend matte system as fast component,good storage stability
Primid(HAA) Based Polyester Resins H602 95/5 20~25 4000~5000 ≥64 180*15 Low cost resin,good flow and mechanical properties
H604 96.5/3.5 18~24 6000~7500 ≥61 180*15
200*10 		Low cost resin,based on hydroxy alkyl amide (HAA) ,good flow ,good overbake resistance to yellowing 
 
                                                           PRODUCT  PARAMETERS
Product Name Powder Coating Polyester Resin
Product Model I902
Product Description I902 is a special carboxyl terminated polyester resin for 93/7, TGIC curing powder coatings cured at 200 ºC. I902 resin is used for outdoor decorative powder coating,include Great weathering resistance,Excellent leveling surface,Good machanical impact testing results ,Excellent outdoor durability,Apply to Matte surface effects.
Product appearance White particles
Viscosity (200 ° C,mpa.s)  4000~5000
Acid Value(mgKOH/g) 30-35
Glass Transition  Temperature ≥64
Curing Ratio 93/7
                                                 APPLY THE INITIAL FORMULA
Components  Net  Wight
I902 558
TGIC 42
Titanium Dioxide 200
Barium Sulfate 177
Flatting Agent 10
Brightener 10
Benzoin 3

                                        EXTRUSION AND  APPLICATION CONDITIONS
Squeeze
Screw 40HZ
Zone 1 temperature 100
Zone 2  temperature 110
Application
Film thickness, substrate 60-80um film thickness, 0.5mm cold rolled steel plate
Gloss ≥90 %
Recoil(kg.cm) 50
Foreflush(kg.cm) 50
Adhesion(grade) 0
Foshan Faxus New Material Company Limited
Please be noticed that the information and testing results represent above is for reference only. Results and figures above will be changed based on different testing conditions. Customers are suggested to design and test the product formula based on the actual conditions of production properties.  

STORAGE CONDITION
 
  • Storage temperature ≤ 30ºC;
  • Storage condition is required to be dry and with good air circulation.
  • Avoiding sunlight exposure.
Outstanding Weathering Resistance Ployester Resin for Metals Coating I-902
PACKAGE

The products are packed by polyethylene bag, 25kg/bag, 1ton/pallet.